PolyJet Material Properties Summary

PolyJet Rubber-like (TangoBlack)PolyJet White (VeroWhitePlus)PolyJet Clear (VeroClear)PolyJet Blue (VeroBlue)PolyJet Black (VeroBlackPlus)PolyJet Polypropylene-like (Durus)
Property ASTM Units Metric Units Imperial
Tensile Strength D-638-03 MPa 0.8-25 psi 116-3,626
Elongation at Break D-638-05 % 25-220 % 25-220
Compressive Set D-395 % 0.5-5 % 0.5-5
Tensile Tear resistance D-624 Kg/cm 2-12 lb/in 18-60
Shore Hardness (A) Scale A Scale A 27-95 Scale A 27-95
Polymerized Density D-792 g/cm3 1.12-1.17
Property ASTM Units Metric Units Imperial
Tensile Strength D-638-03 MPa 55-65 psi 7,250-9,450
Elongation at Break D-638-05 % 10-25 % 10-25
Modulus of Elasticity D-638-04 MPa 2,000-3,000 psi 290,000-435,000
Flexural Strength D-790-03 MPa 75-110 psi 11,000-16,000
Flexural Modulus D-790-04 MPa 2,200-3,200 psi 320,000-465,000
HDT, oC @ 0.45MPa D-648-06 oC 45-50 oF 113-122
HDT, oC @ 1.82MPa D-648-07 oC 45-50 oF 113-122
Izod Notched Impact D-256-06 J/m 20-30 ft lb/in 0.375-0.562
Water Absorption D-570-98 24hr % 1.1-1.5 % 1.1-1.5
Tg DMA, E>> oC 52-54 oF 126-129
Shore Hardness (D) Scale D Scale D 83-86 Scale D 83-86
Rockwell Hardness Scale M Scale M 73-76 Scale M 73-76
Polymerized Density D-792 g/cm3 1.17-1.18  
Ash Content USP281 % 0.23-0.26 % 0.23-0.26
Property ASTM Units Metric Units Imperial
Tensile Strength D-638-03 MPa 50-65 psi 7,250-9,450
Elongation at Break D-638-05 % 10-25 % 10-25
Modulus of Elasticity D-638-04 MPa 2,000-3,000 psi 290,000-435,000
Flexural Strength D-790-03 MPa 75-110 psi 11,000-16,000
Flexural Modulus D-790-04 MPa 2,200-3,200 psi 320,000-465,000
HDT, oC @ 0.45MPa D-648-06 oC 45-50 oF 113-122
HDT, oC @ 1.82MPa D-648-07 oC 45-50 oF 113-122
Izod Notched Impact D-256-06 J/m 20-30 ft lb/in 0.375-0.562
Water Absorption D-570-98 24hr % 1.1-1.5 % 1.1-1.5
Tg DMA, E>> oC 52-54 oF 126-129
Shore Hardness (D) Scale D Scale D 83-86 Scale D 83-86
Rockwell Hardness Scale M Scale M 73-76 Scale M 73-76
Polymerized Density ASTM D792 g/cm3 1.18-1.19  
Ash Content USP281 % 0.02-0.06 % 0.02-0.06
Property ASTM Units Metric Units Imperial
Tensile Strength D-638-03 MPa 50-60 psi 7,250-8,700
Elongation at Break D-638-05 % 15-25 % 15-25
Modulus of Elasticity D-638-04 MPa 2,000-3,000 psi 290,000-435,000
Flexural Strength D-790-03 MPa 60-70 psi 8,700-10,200
Flexural Modulus D-790-04 MPa 1,900-2,500 psi 265,000-365,000
HDT, oC @ 0.45MPa D-648-06 oC 45-50 oF 113-122
HDT, oC @ 1.82MPa D-648-07 oC 45-50 oF 113-122
Izod Notched Impact D-256-06 J/m 20-30 ft lb/in 0.375-0.562
Water Absorption D-570-98 24hr % 1.5-2.2 % 1.15-2.2
Tg DMA, E>> oC 48-50 oF 118-122
Shore Hardness (D) Scale D Scale D 83-86 Scale D 83-86
Rockwell Hardness Scale M Scale M 73-76 Scale M 73-76
Polymerized Density ASTM D792 g/cm3 1.18-1.19  
Ash Content USP281 % 0.21-0.22 % 0.21-0.22
Property ASTM Units Metric Units Imperial
Tensile Strength D-638-03 MPa 51 psi 7,352
Elongation at Break D-638-05 % 18 % 18
Modulus of Elasticity D-638-04 MPa 2192 psi 317,840
Flexural Strength D-790-03 MPa 80 psi 11,542
Flexural Modulus D-790-04 MPa 2200-3200 psi 320,000-465,000
HDT, oC @ 0.45MPa D-648-06 oC 47 oF 117
HDT, oC @ 1.82MPa D-648-07 oC 43 oF 117
Izod Notched Impact D-256-06 J/m 24 ft lb/in 0.45
Water Absorption D-570-98 24hr % 1 % 1
Tg DMA, E>> oC 63 oF 145
Shore Hardness (D) Scale D Scale D 83 Scale D 83
Rockwell Hardness Scale M Scale M 81 Scale M 81
Polymerized Density ASTM D792 g/cm3 1.17-1.18  
Ash content VeroBlackPlus USP281 % 0.01-0.02 % 0.01-0.02
Property ASTM Units Metric Units Imperial
Tensile Strength D-638-03 MPa 20-30 psi 2,900-4,350
Elongation at Break D-638-05 % 40-50 % 40-50
Modulus of Elasticity D-638-04 MPa 1,000-1,200 psi 145,000-175,000
Flexural Strength D-790-03 MPa 34-40 psi 4,350-5,800
Flexural Modulus D-790-04 MPa 1,200-1,600 psi 175,000-230,000
HDT, oC @ 0.45MPa D-648-06 oC 37-42 oF 99-108
HDT, oC @ 1.82MPa D-648-07 oC 32-34 oF 90-93
Izod Notched Impact D-256-06 J/m 40-50 ft lb/in 0.749-0.937
Water Absorption D-570-98 24hr % 1.5-1.9 % 1.5-1.9
Tg DMA, E>> oC 35-37 oF 95-99
Shore Hardness (D) Scale D Scale D 74-78 Scale D 74-78
Rockwell Hardness Scale M Scale M Scale M
Polymerized Density ASTM D792 g/cm3 1.15-1.17  
Ash Content USP281 % 0.10-0.12 % 0.10-0.12

FDM Material Properties

PolyJet Material Properties